Instant Grab Adhesive

XCEL IGA is an instant grab MS Polymer adhesive. It was developed for high strength initial bond. It fixes large panels and heavy objects without support or mechanical fixings, and has high tensile strength. It cures without shrinking, resists vibrations and remains flexible. It is available in 2 colours, grey and white.

  • Permanently flexible

  • Resists Vibrations

  • Adheres to wet and dry surfaces

  • Suitable for indoors and outdoors

  • Paintable

  • ISEGA & HACCP Food Grade Certified

  • Odourless

  • High UV and Fungus resistance

  • Fast curing

  • Cures shrink free

  • High adhesive strength

Technical Information

Raw material basis: MS Polymer
Consistency: Non-slump paste
Specific gravity: approx. 1.30 +/- 0.02
Skin forming time: Less than 20 minutes (at 23ºC; 50% R.H.)
Curing rate: 2-3 mm/24 hr
UV Resistance (ASTM G26): After 2000 hours UV-A no change in appearance or physical properties
Consumption: approx. 50 ml/ linear meter (nozzle diameter: 8mm)
Application temperature: Between 5ºC to 40 ºC
Properties of the cured product: (After one week at 23ºC and 50% R.H.)
Service temperature: -40ºC to +100ºC (short exposure at 140ºC)
100% Modulus (ASTM D412 *Rate = 2”/minute) : 118Psi
Shore A hardness (ISO 868): 57 +/- 5
Max. tensile strength (ASTM D412 *Rate = 2”/minute): 40kg / cm2 / 575 Psi
Peel Strength (ASTM C794) 110 Pli
Elongation: > 110 %
Movement Capability: 25%

These values may vary depending on environmental factors such as temperature, moisture, and type of substrates. The time until complete curing may be extended at lower temperature, lower humidity or increasing film thickness.