Masonry Grab Adhesive

XCEL MGA is a very high strength, high viscosity, one-part elastic adhesive for indoor and outdoor applications based on MS Polymer. Specially designed for fast and non-rigid structural bonding in construction, metal industry and masonry sector, with excellent adhesion to most substrates including brick, concrete, ceramics, marble, wood, melamine, aluminium and metals, and most plastics. Completely neutral and odourless curing.

Permanently flexible
Resists Vibrations
Adheres to wet and dry surfaces
Suitable for indoors and outdoors
Paintable
ISEGA & HACCP Food Grade Certified

Odourless
High UV and Fungus resistance
Fast curing
Cures shrink free
High adhesive strength

Raw material basis:	MS Polymer
Consistency:	Non-slump paste
Specific gravity:	approx. 1.30 +/- 0.02
Skin forming time:	Less than 20 minutes (at 23ºC; 50% R.H.)
Curing rate:	2-3 mm/24 hr
UV Resistance (ASTM G26):	After 2000 hours UV-A no change in appearance or physical properties
Consumption:	approx. 50 ml/ linear meter (nozzle diameter: 8mm)
Application temperature:	Between 5ºC to 40 ºC
Properties of the cured product:	(After one week at 23ºC and 50% R.H.)
Service temperature:	-40ºC to +100ºC (short exposure at 140ºC)
100% Modulus (ASTM D412 *Rate = 2”/minute) :	118Psi
Shore A hardness (ISO 868):	57 +/- 5
Max. tensile strength (ASTM D412 *Rate = 2”/minute):	40kg / cm2 / 575 Psi
Peel Strength (ASTM C794)	110 Pli
Elongation at break (ISO 37):	> 110 %
Movement Capability:	25%

These values may vary depending on environmental factors such as temperature, moisture, and type of substrates. The time until complete curing may be extended at lower temperature, lower humidity or increasing film thickness.